UVCLX UV Cure Conformal Coating Xtra

In Stock

UVCLX is part of the new generation of UV Cure Conformal Coatings developed by Electrolube to offer the highest levels of protection whilst maintaining a fast processing time. Applied via a selective coating machine, UVCLX builds on the speed of a traditional UV Cure Coating, being touch dry after just a short exposure to the correct wave length of UV light. A full cure is guaranteed in less than 24 hours by virtue of the secondary chemical cure mechanism. The chemical cure ensures that even shadowed areas are fully cured in a matter of hours. This is in stark contrast to other traditional UV Cure Coatings that can require weeks for a complete cure; (some shadowed areas will even remain uncured). UVCLX therefore ensures reduced work in progress times.


Approvals RoHS Compliant (2015/863/EU): Yes
REACH Compliant: Yes
IPC-CC-830 Rev. C: Meets Requirements
UL746-QMJU2: Approved File Number: E138403
Liquid Properties Appearance: Opaque Green Liquid
Density @ 20°C (g/ml): 1.31 (mixed)
Flash Point: >100⁰C
Min. Solids Content (1hr @80˚C): >99%
Mix Ratio: 2:1 v/v
Mixed System Viscosity @ 25˚C: Sprayable
Mixed Useable Life @ 20°C: 5 Minutes
Recommended Drying Time: UV (see curing instructions – page 2)
Touch Dry Time at 20°C: 10 Minutes
Dry Film Coating Colour: Opaque Green
Recommended Coating Thickness: 200-350µm
Temperature Range: -40 to +130⁰C
Thermal Shock Range: -65 to +125⁰C
Thermal Shock (1000 cycles): No cracking, blistering or delamination*
Shore Hardness: A98
Elongation at Break (BS EN ISO 537): 40%
Elastic Modulus (BS EN ISO 537): 18.5 MPa @ 20˚C
Tensile Strength (BS EN ISO 537): 45 MPa @ 20˚C
Dielectric Strength: 90 kV/mm
Surface Insulation Resistance: 1 x 1015 Ω
Moisture Resistance (IPC-CC-830): 9.34 x 109 Ω
Flammability: UL94 V-0 Approved